Specification |
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 82-96;
Density,g/cm3: 1.12;
100% Modulus,MPa: 7-10;
300% Modulus,MPa: 14-19;
Tensile Strength,MPa: 38-50;
Tear Strength,MPa: 90-130;
Elongation at Break,%: 350-500;
Tear Strength,Kn/M: 90-130;
|
CAS No.: 68648-82-8;
Formula: C9h11cl7;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Full Name: Chlorinated Polyvinyl Chloride Resin;
Brand: Gaoxin, Yada, Suneight, Pujie, HEC, Leeman, Xiangsheng;
Similar Brand: Kenaka, Sekisui, Lubrizol, Kemone;
Exterior: White / Pale Yellow Powder;
Application: Pipes / Pipe Fittings;
Production Process: Acid Phase Method / Aqueous Suspension Method;
Chlorine Content: 66%-68%;
30 Mesh Sieving Rate: ≥99.0%;
Volatile Content: ≤0.35%;
Vicat Softening Temperature: 115-130ºC;
Thermal Decomposition Temperature: ≥120ºC;
Tensile Strength: 52MPa;
Bulk Density: 0.5-0.7g/cm3;
Tensile Modulus of Elasticity: 2482-2758;
|
CAS No.: 68648-82-8;
Formula: C9h11cl7;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Full Name: Chlorinated Polyvinyl Chloride Resin;
Brand: Gaoxin, Yada, Suneight, Pujie, HEC, Leeman, Xiangsheng;
Similar Brand: Kenaka, Sekisui, Lubrizol, Kemone;
Exterior: White / Pale Yellow Powder;
Application: Pipes / Pipe Fittings;
Production Process: Acid Phase Method / Aqueous Suspension Method;
Chlorine Content: 66%-68%;
30 Mesh Sieving Rate: ≥99.0%;
Volatile Content: ≤0.35%;
Vicat Softening Temperature: 115-130ºC;
Thermal Decomposition Temperature: ≥120ºC;
Tensile Strength: 52MPa;
Bulk Density: 0.5-0.7g/cm3;
Tensile Modulus of Elasticity: 2482-2758;
|
CAS No.: 68648-82-8;
Formula: C9h11cl7;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Full Name: Chlorinated Polyvinyl Chloride Resin;
Brand: Gaoxin, Yada, Suneight, Pujie, HEC, Leeman, Xiangsheng;
Similar Brand: Kenaka, Sekisui, Lubrizol, Kemone;
Exterior: White / Pale Yellow Powder;
Application: Pipes / Pipe Fittings;
Production Process: Acid Phase Method / Aqueous Suspension Method;
Chlorine Content: 66%-68%;
30 Mesh Sieving Rate: ≥99.0%;
Volatile Content: ≤0.35%;
Vicat Softening Temperature: 115-130ºC;
Thermal Decomposition Temperature: ≥120ºC;
Tensile Strength: 52MPa;
Bulk Density: 0.5-0.7g/cm3;
Tensile Modulus of Elasticity: 2482-2758;
|
CAS No.: 68648-82-8;
Formula: C9h11cl7;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Full Name: Chlorinated Polyvinyl Chloride Resin;
Brand: Gaoxin, Yada, Suneight, Pujie, HEC, Leeman, Xiangsheng;
Similar Brand: Kenaka, Sekisui, Lubrizol, Kemone;
Exterior: White / Pale Yellow Powder;
Application: Pipes / Pipe Fittings;
Production Process: Acid Phase Method / Aqueous Suspension Method;
Chlorine Content: 66%-68%;
30 Mesh Sieving Rate: ≥99.0%;
Volatile Content: ≤0.35%;
Vicat Softening Temperature: 115-130ºC;
Thermal Decomposition Temperature: ≥120ºC;
Tensile Strength: 52MPa;
Bulk Density: 0.5-0.7g/cm3;
Tensile Modulus of Elasticity: 2482-2758;
|