Specification |
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Isostatic Pressing Type;
Size: Middle;
Color: White;
Customized: Customized;
Raw Material: Australia;
Al2O3: 92%,95%;
Hardness: 9mohs;
Density: 3.6g/cm3;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|