Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials, Top Grade;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Refractory Bricks High Alumina Brick;
Model Number: High Alumina Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow;
Application: Reverberatory Furnace;
Al2O3 Content (%): 48%-85%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Long Time Materials, Instant Materials;
Type: Refractory Material, Ceramic Crucible;
Shape: Crucible, Conical, Circular, Cylindrical;
Material: Alumina Cement, Clay;
Refractoriness: 1580< Refractoriness< 1770;
Color: White, Light Yellow;
Name: High Temperature Metal Analysis Clay Crucible;
Max. Working Temperature: 1650 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Purpose: Gold Smelting and Assaying;
Size: 30g, 40g, 45g, 50g, 65g;
Usage: Melting, Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing, Paper Carton Packing;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Plate;
Material: Alumina Ceramic;
Max Working Temperature: 1600c;
Thermal Shock Resistance: 180-220t;
Special: Ceramic Crucible Part;
Product: Alumina Parts;
Name: Machine Alumina Ceramic Part;
Raw Material: 60-99.7% Alumina Ceramic;
Item: Alumina Ceramics Part;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Plate;
Material: Alumina Ceramic;
Max Working Temperature: 1600c;
Thermal Shock Resistance: 180-220t;
Special: Ceramic Crucible Part;
Product: Alumina Parts;
Name: Machine Alumina Ceramic Part;
Raw Material: 60-99.7% Alumina Ceramic;
Item: Alumina Ceramics Part;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Plate;
Material: Alumina Ceramic;
Max Working Temperature: 1600c;
Thermal Shock Resistance: 180-220t;
Special: Ceramic Crucible Part;
Product: Alumina Parts;
Name: Machine Alumina Ceramic Part;
Raw Material: 60-99.7% Alumina Ceramic;
Item: Alumina Ceramics Part;
|