Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Instant Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Product Name: Alumina Silicon Carbide Carbon Castable;
Color: Grey;
Cold Crushing Strength(MPa): 20~80MPa;
Application: Industrial Furnaces;
Function: Functional Refractories;
Maximum Service Temperature: 1400-1650;
Al2O3: 50%-90%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|