Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Sio2 Content: 50%~65%;
Al2O3 Content (%): 38-42%;
MGO Content (%): 0.8-1.2;
Refractoriness (Degree): 1580< Refractoriness< 1770;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Insulation,Refractory Liner;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 2.3-2.4kg/M3;
Permanent Linear Change %: 0~+0.2;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Alumina Block;
Raw Material: Clay;
Application: Backing Insulation for Dense Bricks in Kilns;
Density: 0.6g/cm3, 0.7g/cm3, 0.8g/cm3, 0.9g/cm3.etc;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Alumina Block;
Raw Material: Clay;
Application: Backing Insulation for Dense Bricks in Kilns;
Density: 0.6g/cm3, 0.7g/cm3, 0.8g/cm3, 0.9g/cm3.etc;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Alumina;
Alumina Content: >99%;
Size: Od 8-50;
Color: White, Pink Cream;
End: Oec or Beo;
Application: High Temperature Resistant, High Wear Resistance;
Finish: Collar, Slot, Curve;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application: Drying Tower of Chemical Factory,etc;
Colour: Many Colours;
|