Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Sio2 Content: 50%~65%;
Al2O3 Content (%): 38-42%;
MGO Content (%): 0.8-1.2;
Refractoriness (Degree): 1580< Refractoriness< 1770;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Insulation,Refractory Liner;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 2.3-2.4kg/M3;
Permanent Linear Change %: 0~+0.2;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Steatite;
Color: White Pink,Grey;
Type of Bead: Dome Bead,Flat Bead,Fish Spine;
Appreance: Top Groove,Bottom Groove,No Groove;
Property: Thermal Expansion Coefficient, Excellent Electrica;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Raw material: alumina, other materials;
alumina: 70%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.3-2.35g/cm3;
Apparent Porosity: 15%;
Tsr 950ºC: 15cycle;
Rul: 1500;
CCS MPa: 80;
|