Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3 Content (%): ≥43%;
Sio2 Content (%): 50-65%;
Bulk Density G/Cm³: 2.35;
Apparent Porosity: 23%;
Fe2o3: 2%-4%;
Variation of Re-Burning Line 1400: +0.1/-0.4;
Application: Bottom of Glass Furnace;
Raw Material: Calcined Bauxite;
Cold Crushing Strength MPa: 50;
|
Refractoriness (℃): 1050ºC;
Feature: Long Time Materials;
Type: Calcium Silicate Boards;
Shape: Block;
Material: Sio2, Cao;
Edge: Square;
Application: Building, Furnace.etc;
Thickness: 25mm, 50mm, 100mm or Customized;
Character: Non-Asbestos;
Colour: White;
Appearance: Plate or Board;
Density: 170-300kg/M³;
Key Properties: Low Thermal Conductivity&Good Compression Strength;
|
Refractoriness (℃): 1050ºC;
Feature: Long Time Materials;
Type: Calcium Silicate Boards;
Shape: Block;
Material: Sio2, Cao;
Edge: Square;
Application: Building, Furnace.etc;
Thickness: 25mm, 50mm, 100mm or Customized;
Character: Non-Asbestos;
Colour: White;
Appearance: Plate or Board;
Density: 170-300kg/M³;
Key Properties: Low Thermal Conductivity&Good Compression Strength;
|
Refractoriness (℃): 1050ºC;
Feature: Long Time Materials;
Type: Calcium Silicate Boards;
Shape: Block;
Material: Sio2, Cao;
Edge: Square;
Application: Building, Furnace.etc;
Thickness: 25mm, 50mm, 100mm or Customized;
Character: Non-Asbestos;
Colour: White;
Appearance: Plate or Board;
Density: 170-300kg/M³;
Key Properties: Low Thermal Conductivity&Good Compression Strength;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Alumina;
Application Zone: Transition Zone;
Bulk Density: 2.9;
Apparent Porosity: 16;
Tsr: 100;
Rul: 1000;
CCS: 65;
Thermal Conductivity: 3.713;
|