| Specification |
File Format: STL;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory;
Printer Material: Gypsum,Resin,PLA,Plastic,Metal,Glass;
Forming Technology: SLA,SLS,Fdm,Mjf,Slm;
Surface Treatment: Painting/Sand Blasting/Electroplating/Polishing;
Sample: Contact Customer Service;
Quality: 100% Inspection on Critical Dimensions;
Delivery Date: 5-15days;
Customization: Customized;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|
File Format: STEP;
Application: Auto and Motorcycle Accessory, Household Appliances, Furniture, Hardware, Machinery Accessory, Aerospace Industry;
Printer Material: Metal;
Nozzle Number: 4;
Forming Technology: 3DP;
Heat Deflection: 88-89;
Glass Transition Temperature: 105;
Vicat Softening Temperature: 100;
Coefficient of Thermal Expansion: 120;
Thermal Conductivity (W/M.K)): 0.1;
Specific Heat Capacity(J/Kg.K): 900;
Tensile Strength MPa: 42.5-44.8;
Modulus of Elasticity(Gpa): 2.0-2.6;
Flexural Strenght(MPa): 60.6-73.1;
Flexural Modulus(Gpa)): 2.25-2.28;
|