Specification |
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Cold Crushing Strength: ≥40MPa;
Density: ≥2.9 g/cm3;
Apparent Porosity: ≤3%;
C: 10;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material, Nickel Plate;
Shape: Plate;
Material: Alumina Block, as Requried;
Product Type: Coil, Rold, Wire;
Carbon Content: as Requried;
PCD: as Requried;
Et: as Requried;
Hole: as Requried;
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >98%;
Alloy: Alloy;
Powder: Not Powder;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Alumina Block;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material, Nickel Plate;
Shape: Plate;
Material: Alumina Block, as Requried;
Product Type: Coil, Rold, Wire;
Carbon Content: as Requried;
PCD: as Requried;
Et: as Requried;
Hole: as Requried;
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >98%;
Alloy: Alloy;
Powder: Not Powder;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Sio2 Content: 50%~65%;
Al2O3 Content (%): 38-42%;
MGO Content (%): 0.8-1.2;
Refractoriness (Degree): 1580< Refractoriness< 1770;
Cro Content (%): 0.1~0.3%;
Standard Size: 230*114*65mm;
Application: Insulation,Refractory Liner;
Fe2o3 %: 1.0;
Apparent Porosity %: 20;
Bulk Density g/cm3: 2.3-2.4kg/M3;
Permanent Linear Change %: 0~+0.2;
|