Specification |
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
Process: as Required;
Color: Silver;
Supply Type: in-Stock Items;
Steel Grade: 50A600 50A800;
|
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.15-0.30;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 900~1200mm;
Weight: 2~5t;
|
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.15-0.30;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 900~1200mm;
Weight: 2~5t;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508;
Nominal Thickness: 0.20mm,0.25mm,0.27mm,0.30mm,0.35mm,0.50mm,0.65mm;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508;
Nominal Thickness: 0.20mm,0.25mm,0.27mm,0.30mm,0.35mm,0.50mm,0.65mm;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
|