| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: 7200mm, 3600mm etc;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c, 1260c, 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Fireproof;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1260-1600 ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2, Cr2o3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Double- Needled;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Regular Size in mm: 7320 * 610/1220 * 25mm, 3660 * 610/1220 *;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Application: Furnace Hot Face Repairs, Boiler Insulation;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1260 - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2 ,Cr2o3;
Shape: Module, Z-Block;
Manufacturing Technique: Folded by Needle Blanket and Anchor;
Kind: High Purity Ceramic Fiber;
Regular Size: 305 X 305mm;
Thickness Available: 100 to 305 mm;
Special Size: Can Be Customized;
Density: 160 192 ,210 ,230 Kg/M3;
Feature: Faster Insulation ,Low Heat Storage;
Application: High Temperature Furnace ,Kiln and Heater Linings;
H.S.Code: 68061010;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1260 - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2 ,Cr2o3;
Shape: Module, Z-Block;
Manufacturing Technique: Folded by Needle Blanket and Anchor;
Kind: High Purity Ceramic Fiber;
Regular Size: 305 X 305mm;
Thickness Available: 100 to 305 mm;
Special Size: Can Be Customized;
Density: 160 192 ,210 ,230 Kg/M3;
Feature: Faster Insulation ,Low Heat Storage;
Application: High Temperature Furnace ,Kiln and Heater Linings;
H.S.Code: 68061010;
|