Specification |
Usage: Thermal Insulation Coatings, Friction Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: as Your Request;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c - 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Non-Inflammable;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Kind: Ordinary Ceramic Fiber;
Length: 1200/1000/900mm;
Width: 1000/600/500mm;
Thickiness: 5-100mm;
Ultimate Strength: 0.7MPa;
Chemical Composition: Al2O3+Sio2;
Thermal Conductivity: 0.085(400c)/0.132(800c);
Shrinkage (1800f, 3h: -3%;
Color: White;
Application: Liners of Industrial Furnace;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Forming;
Kind: High Purity Ceramic Fiber;
Length: 1200/1000/900mm;
Width: 1000/600/500mm;
Thickiness: 5-100mm;
Ultimate Strength: 0.7MPa;
Chemical Composition: Al2O3+Sio2;
Thermal Conductivity: 0.085(400c)/0.132(800c);
Shrinkage (1800f, 3h: -3%;
Color: White;
Application: Liners of Industrial Furnace;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Kind: High Purity Ceramic Fiber;
Length: 1200/1000/900mm;
Width: 1000/600/500mm;
Thickiness: 5-100mm;
Ultimate Strength: 0.7MPa;
Chemical Composition: Al2O3+Sio2;
Thermal Conductivity: 0.085(400c)/0.132(800c);
Shrinkage (1800f, 3h: -3%;
Color: White;
Application: Liners of Industrial Furnace;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Inorganic Wet Technology;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Paper;
Length: as Per Customer's Request;
Width: From 50mm;
Thickness: 0.5-10mm;
Density: 180-210kg/M3;
Color: White;
Working Temperature: 1050c;
Fiber Diameter: 2-5um;
Thermal Conductivity: 0.160~0.170(W/K.M.)(250kgs/M3);
Shrinkage (1800ºF, 3h): -3(24hours);
|