Specification |
Usage: Thermal Insulation Coatings, Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Max Thickness: 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Smell: Inorganic Type Has No Smell;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler Heat Insulation Liner;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material, Heat Insulation;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Rope;
Manufacturing Technique: Ceramic Square Braided Rope;
Kind: High Purity Ceramic Fiber;
Near Port: Shanghai, Ningbo;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material, Heat Insulation;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Rope;
Manufacturing Technique: Ceramic Fiber Lagging Rope;
Kind: High Purity Ceramic Fiber;
Near Port: Shanghai, Ningbo;
|
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Board;
Color: White;
Temperature: 1100-1430;
Density: 260-320;
Tensilestrengty: 0.5;
Package: Carton;
Place of Origin: Zhejiang;
|
Usage: High Temperature Insulating Material;
Colour: White;
Working Temperature: 1050ºC--1350ºC;
Temprature Classification: 1600ºC, 1500ºC, 1400ºC, 1260ºC;
Fiber Diameter: 3-5um;
Grade: St (Standard);
Ultimate Strength (≥ MPa): 0.5;
Applicatio: Refractory;
Thermal Conductivity: 0.17;
Density (Kg/M3): 96-128;
|