Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: 7200mm, 3600mm etc;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c, 1260c, 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Fireproof;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Board;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1100c/1260c/1360c/1430c;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
Keyword: Refractory Ceramic Fiber Board Heat Insu;
Type: Containing Zirconium Ceramic Fiber;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Ahlmirla Fibre;
Working Temperature: 1000 Degree;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|