Specification |
Usage: Concrete;
Material: 100% Polypropylene;
Feature: Reinforcement;
Fiber Type: Staple;
Pattern: as Per Your Request;
Color: White;
Width: as Per Your Request;
Function: Reinforcement;
Structure: as Per Your Request;
Product Name: Concrete Reinforcement Fiber PP Fiber Monofilament;
Length: Times of 4mm/6mm with 1mm More or Less;
Crack Elongation: 20+/-5%;
Fiber Diameter: 20um-30um;
Raw Material: 100% Virgin Polypropylene;
Tensile Strength: 450MPa Min;
Melting Point(C Deg. ): 160-170;
Density(g/cm3): 0.91+/-0.01;
Acid &Alkali Resistance: Strong;
|
Usage: Concrete, Filling Material, Spinning;
Material: 100% Polyester;
Feature: Abrasion-Resistant, Anti-Distortion, Anti-Static, Heat-Resistant;
Fiber Type: Filament;
Color: White;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 10~25um;
Modulus of Elasticity: 8000MPa;
Tensile Strength: More Than 900MPa;
Density: 1.36g/cm3;
Material Property: 100%Modified Polyester;
|
Usage: Concrete, Filling Material, Spinning;
Material: 100% Polyacrylonitrile (Pan);
Feature: Abrasion-Resistant, Anti-Distortion, Heat-Resistant;
Fiber Type: Filament;
Color: Light Yellow;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Equivalent Diameter: 12~20um;
|
Usage: Concrete, Filling Material, Spinning;
Material: Polyvinyl Alcohol;
Feature: Abrasion-Resistant, Anti-Distortion, Heat-Resistant;
Fiber Type: Filament;
Color: Light Yellow;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 15.0 Um;
Breaking Strength: 1600MPa;
Dry Breaking Tenacity(Cn/Dtex)≥: 11;
Hot Water ResistanceºC≥: 104;
E-Modulus (Cn/Dtex)≥: 290;
|
Usage: Concrete, Filling Material, Spinning;
Material: Polyvinyl Alcohol;
Feature: Abrasion-Resistant, Anti-Distortion, Heat-Resistant;
Fiber Type: Filament;
Color: Light Yellow;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 15.0 Um;
Breaking Strength: 1600MPa;
Dry Breaking Tenacity(Cn/Dtex)≥: 11;
Hot Water ResistanceºC≥: 104;
E-Modulus (Cn/Dtex)≥: 290;
|