Specification |
Application: Industrial Ceramic, Electronic Ceramic;
Material: Alumina Ceramic;
Delivery: 30 Days;
Thermal Conductivity: Min 24 W/Mk;
Young's Modulus: 340 Gpa;
Thickness: 0.2-2mm;
Forming Method: Tape Casting;
Type: Ceramic Plate, Ceramic Plates;
|
Application: Industrial Applications;
Function: Wear Resistant;
Material: Alumina Ceramic;
Process: Porcelain Ceramic Plate;
Pores Diameter: 1-5, 15, 30, 40, 50, 100μm, Customized;
Color: White, Grey, Brown;
Density: 2.3-2.5g/cm3;
Compressive Strength: ≥600;
Porosity: 40%;
Porous Ceramics Application: Vacuum Chuck;
Advantage: Corrosion Resistance, Have Pore Size;
Hardness (Hra): ≥50;
Al2O3: ≥80%;
Flexural Strength: 40MPa;
Operating Pressure: ≤10 MPa;
Acid Resistance: ≤10.0 Mg/Cm2;
Alkali Resistance: ≤20.0 Mg/Cm2;
|
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Flexural Strength: 300MPa;
Shape: Plate Disc;
Max Use Temperature: 1600°c;
Color: White;
Processing Service: Welding, Moulding;
Material Option: 96%, 99%, 99.7% Alumina;
Purity: 95%;
Type: Ceramic Plates;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Flexural Strength: 358MPa;
Shape: Customized;
Plater Layer: Ni, Cu, Au, etc.;
Color: White+Metal;
Max Use Temperature: 1600c;
Compressive Strength: 2300MPa;
Processing Service: Moulding;
Plated Thickness: 2-9um;
Coating Layer: Mo/Mn;
Coating Thickness: 8-30um;
Material Composition: Alumina, Al2O3;
Speciality: High Insulation;
Type: Ceramic Plates;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Max Use Temperature: 1600;
Color: Black;
Compressive Strength: 3200;
Water Absorption: 0;
Thermal Conductivity: 150;
Processing Service: Moulding;
Density: >3.1g/cm3;
Theramal Shock Resistance: 300;
Flexural Strength: 480;
Vickers Hardness: 24;
Surface Treatment: Full Body Tiles;
Type: Ceramic Plates;
|