Specification |
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 0.1-1, 1-3, 3-5, 5-8;
Usage: Ceramic, Polishing, Abrasive, Refractory;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 16-220;
Usage: Ceramic, Polishing, Abrasive, Refractory;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 0.1-1, 1-3, 3-5, 5-8;
Usage: Ceramic, Polishing, Abrasive, Refractory;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Origion: China;
Kind: Factory Supply;
Sample: Free;
Package: 25kg;
MSDS: Yes;
Grade: Top;
Material: Alumina Oxide;
|
Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Raw Materials;
Color: Brilliant White Powder/Granular;
Morse Hardness: 9;
Grain Density: 3.75-3.95g/cm3;
Size: 0.1-1, 1-3, 3-5, 5-8;
Usage: Ceramic, Polishing, Abrasive, Refractory;
HS Code: 2818101000;
Fe2o3: 0.03%-0.04%;
Sio2: 0.05%;
Na2o: <0.3%;
Al2O3: 99%;
Material: Alumina Oxide;
|