Specification |
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Flexural Strength: >1000 MPa;
Purity: 99%;
Type: Ceramic Parts;
Thermal Shock Resistance: Good;
Water Absorption: 0;
Thermal Conductivity: 30;
Maximum Use: 1700;
Processing Service: Moulding;
Density: 3.7;
Flexural Ctrength: 400;
Compressive Ctrength: 3150;
Volume of Jar: 50ml;
|
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Type: Ceramic Rings;
Water Absorption: 0;
Color: White;
Maximum Use Temperature: 1400-1500;
Processing Service: Moulding;
Density: 3.8-6;
Sealed Ink Cup Application: Pad Printing;
Volume Resistivity: More Than 10^14;
Advantage: Wear Resistant;
Thermal Shock Resistance: 300-500;
Compressive Strenght: 2200-2900;
|
Application: Aerospace, Electronics, Medical, Industrial Ceramic;
Type: Ceramic Rings;
Water Absorption: 0;
Color: White;
Maximum Use Temperature: 1400-1500;
Processing Service: Moulding;
Density: 3.8-6;
Sealed Ink Cup Application: Pad Printing;
Volume Resistivity: More Than 10^14;
Advantage: Wear Resistant;
Thermal Shock Resistance: 300-500;
Compressive Strenght: 2200-2900;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial Ceramic;
Flexural Strength: >1000 MPa;
Purity: 99%;
Type: Ceramic Part;
Shape: Tube;
Max Use Temperature: 1500°c;
Color: White;
Processing Service: Moulding;
Density: 3.6g/cm3;
|