Specification |
Application: Continus Casting,Sintering,Smelting;
Carbon Content: High-Carbon;
Composition: Carbon;
Crystal Morphology: Artificial Graphite;
Forming Way: Isostatic Graphite;
Grade: Industrial Grade;
Type: Isostatic Graphite;
Chemical Composition: Carbon;
Density: 1.9g/cm3;
Er: 8~10 Ω·m;
Thermal Conductivity: 135W/M.K;
Cte: 5.1;
Shore Hardness: 53 Hsd;
Flexural Strength: 55 MPa;
Compressive Strength: 95 MPa;
Ash: 50 Ppm;
Porosity: 11%;
Particle Size: 8~10 Micron;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Composition: C;
Crystal Morphology: CVD;
Forming Way: Chemical;
Grade: Industrial Grade;
Type: Specialty Graphite Or Special Graphite;
Purity: 97%;
Average Diameter: 10-20nm;
Length: <50μm;
Specific Surface Area: 240-300m2/G;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Composition: C;
Crystal Morphology: CVD;
Forming Way: Chemical;
Grade: Industrial Grade;
Type: Specialty Graphite Or Special Graphite;
Purity: 97%;
Average Diameter: 10-20nm;
Length: <50μm;
Specific Surface Area: 240-300m2/G;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Composition: C;
Crystal Morphology: CVD;
Forming Way: Chemical;
Grade: Industrial Grade;
Type: Specialty Graphite Or Special Graphite;
Purity: 97%;
Average Diameter: 10-20nm;
Length: <50μm;
Specific Surface Area: 240-300m2/G;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Composition: C;
Crystal Morphology: CVD;
Forming Way: Chemical;
Grade: Industrial Grade;
Type: Specialty Graphite Or Special Graphite;
Purity: 97%;
Average Diameter: 10-20nm;
Length: <50μm;
Specific Surface Area: 240-300m2/G;
|