| Specification |
Casting Method: Vacuum Casting;
Process: Lost Wax Casting;
Molding Technics: Silica Sol Process;
Application: Turbojet Engine;
Material: Inconel713c;
Surface Preparation: Sand Blast;
Surface Roughness: Ra3.2;
Machining Tolerance: +/-0.01mm;
Standard: ASTM;
Tensile Test Temperature: Above 900 Degree;
Tensile Strength of High Temperature: Above 830MPa;
Elongation of High Temperature: Above 3%;
Persistent Creep Temperature at High Tem: Above 975 Degree;
Creep Tensile Strength at High Temperatu: Above 225MPa;
High Temperature Duration: Above 40h;
Test of Surface Defect: Fpt;
Test of Internal Defect: X-ray;
Test of Size: CMM;
|
Casting Method: Directional Crystallization;
Process: Lost Wax Casting;
Molding Technics: Pressure Casting;
Application: Machinery Parts;
Material: Stainless Steel;
Surface Preparation: Polishing;
Surface Roughness: Ra12.5;
Machining Tolerance: +/-0.01mm;
Standard: GB;
CNC Machining or Not: CNC Machining;
Type: Broaching, Drilling, Etching / Chemical Machining;
Material Capabilities: Hardened Metals, Stainless Steel, Steel,Iron;
Micro Machining or Not: Micro Machining;
Place of Origin: Qingdao,China;
Optional Material: Stainless Steel, Carbon Steel,Brass, Aluminum etc.;
Machine: CNC Center;
Surface: as Customers' Requirements;
Inspection: 100%;
Min Tolerance: +/-0.01mm;
|
Casting Method: Directional Crystallization;
Process: Lost Wax Casting;
Molding Technics: Pressure Casting;
Application: Machinery Parts;
Material: Stainless Steel;
Surface Preparation: Polishing;
Surface Roughness: Ra3.2;
Machining Tolerance: +/-0.01mm;
Standard: GB;
CNC Machining or Not: CNC Machining;
Type: Broaching, Drilling, Etching / Chemical Machining;
Material Capabilities: Hardened Metals, Stainless Steel, Steel,Iron;
Micro Machining or Not: Micro Machining;
Place of Origin: Qingdao,China;
Optional Material: Stainless Steel, Carbon Steel,Brass, Aluminum etc.;
Machine: CNC Center;
Surface: as Customers' Requirements;
Inspection: 100%;
Min Tolerance: +/-0.01mm;
|
Casting Method: Directional Crystallization;
Process: Lost Wax Casting;
Molding Technics: Pressure Casting;
Application: Machinery Parts;
Material: Stainless Steel;
Surface Preparation: Polishing;
Surface Roughness: Ra12.5;
Machining Tolerance: +/-0.01mm;
Standard: GB;
CNC Machining or Not: CNC Machining;
Type: Broaching, Drilling, Etching / Chemical Machining;
Material Capabilities: Hardened Metals, Stainless Steel, Steel,Iron;
Micro Machining or Not: Micro Machining;
Place of Origin: Qingdao,China;
Optional Material: Stainless Steel, Carbon Steel,Brass, Aluminum etc.;
Machine: CNC Center;
Surface: as Customers' Requirements;
Inspection: 100%;
Min Tolerance: +/-0.01mm;
|
Casting Method: Directional Crystallization;
Process: Lost Wax Casting;
Molding Technics: Pressure Casting;
Application: Machinery Parts;
Material: Stainless Steel;
Surface Preparation: Polishing;
Surface Roughness: Ra12.5;
Machining Tolerance: +/-0.01mm;
Standard: GB;
CNC Machining or Not: CNC Machining;
Type: Broaching, Drilling, Etching / Chemical Machining;
Material Capabilities: Hardened Metals, Stainless Steel, Steel,Iron;
Micro Machining or Not: Micro Machining;
Place of Origin: Qingdao,China;
Optional Material: Stainless Steel, Carbon Steel,Brass, Aluminum etc.;
Machine: CNC Center;
Surface: as Customers' Requirements;
Inspection: 100%;
Min Tolerance: +/-0.01mm;
|