| Specification |
Material: Polyurethane rubber;
Kind: Solid bar;
Tensile Strength: ≤50Mpa;
Shore A: 80/ 92;
Temperature Range: -20 ºC - +80ºC;
Load Range: more than 2x10^6;
Rebound resilience: 48%/43%;
|
Material: PTFE;
Kind: Plastic Bar;
Water Absorption: ＜0.01%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 30~40MPa;
Style: Extruded PTFE Rod;
Diameter: 3mm~300mm;
Length: 100mm ~ 3000mm;
Density: 2.1 ~ 2.3 g/cm3;
Temp: -180 ~ + 260;
Crack Elongation: >150%;
Productivity: 100ton/Month;
MOQ: 200kg;
Color: White;
Fillers: Fiberglass, Carbon, Graphite, Bronze;
Materials: PTFE Material;
Filler: Glass, Carbon, Graphite, Bronze;
Style 1: Extruded PTFE Rod;
Style 2: Moulded PTFE Rod;
|
Material: PVC;
Kind: Hard Plastic Rods;
Water Absorption: ＜0.01%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 41~50MPa;
Sizes: 10mm-300mm;
Stardard Color: Dark Grey(Ral7011),Balck White Red;
|
Material: PTFE;
Kind: Plastic Bar;
Water Absorption: ＜0.01%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 30~40MPa;
Style: Extruded PTFE Rod;
Diameter: 3mm~300mm;
Length: 100mm ~ 3000mm;
Density: 2.1 ~ 2.3 g/cm3;
Temp: -180 ~ + 260;
Crack Elongation: >150%;
Productivity: 100ton/Month;
MOQ: 200kg;
Color: White;
Fillers: Fiberglass, Carbon, Graphite, Bronze;
Materials: PTFE Material;
Filler: Glass, Carbon, Graphite, Bronze;
Style 1: Extruded PTFE Rod;
Style 2: Moulded PTFE Rod;
|
Material: PTFE;
Kind: Plastic Bar;
Water Absorption: ＜0.01%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 30~40MPa;
Style: Extruded PTFE Rod;
Diameter: 3mm~300mm;
Length: 100mm ~ 3000mm;
Density: 2.1 ~ 2.3 g/cm3;
Temp: -180 ~ + 260;
Crack Elongation: >150%;
Productivity: 100ton/Month;
MOQ: 200kg;
Color: White;
Fillers: Fiberglass, Carbon, Graphite, Bronze;
Materials: PTFE Material;
Filler: Glass, Carbon, Graphite, Bronze;
Style 1: Extruded PTFE Rod;
Style 2: Moulded PTFE Rod;
|