Specification |
CAS No.: Inv-V411m;
Formula: Inv-V411m;
EINECS: Inv-V411m;
Molecular Principal Chain: Element Organic Polymer;
Color: Light Yellow Transparent Liquid;
Tensile Strength (MPa): 85;
Tensile Modulus (Gpa): 3.1;
Elongation at Break (%): 4.0;
Bending Strength (MPa): 140;
Flexural Modulus (Gpa): 3.1;
Impact Toughness (Kj/M2): 7;
Package Size Per Unit Product: 50.00cm * 100.00cm * 50.00cm;
Gross Weight Per Unit Product: 220.000kg;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-82;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 5-35;
300% Modulus,MPa: 12-43;
Tensile Strength,MPa: 35-60;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|