Specification |
Material: Ceramics;
Content: 95% Alumina Content;
Usage: Grind, Grind Material in Chemicals , Paints , Iron Ore;
Processing Type: Isostatic Pressing Type;
Size: 31*31mm;
Color: White;
Customized: in Stock;
Item: Alumina Grinding Cylinder;
Materials: Alumina;
Alumina Content: 95%;
Type: High-Alumina;
Diameter: 21*21mm 31*31mm;
Grinding Situation: Dry Grinding , Wet Griding;
Feature: High Hardness, High Density and Anticorrosion;
Application: Ball Mill, Pebble Mill ,Paints Grinding;
Field: Ceramic,Metallurgy, Glass, Porcelain, Enamel;
OEM: Accept;
Self-Wear Loss: 0.06‰;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|
Material: Zirconia;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Zro2(%): >94;
Y2o3(%): 6;
Wear Loss(G/Kgh): <1.3;
Packing Density Kg/L: 3.7~3.9;
Bulk Density g/cm3: 5.95~6.0;
Hardness (Hv) Gpa: 8;
Crushing Strength N: 16000;
Sphericity %: ≥95;
Standard Size mm: 0.3-30;
Packing: 25kg;
|