| Specification |
Shotblast Type: Shot Blasting;
Shotblast Material: Steel Shot;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Aircraft Parts;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Chemical;
Name: Steel Shot;
Shape: Spherical/Round;
Hardness in HRC: Gp41-50HRC;Gl50-55HRC;Gh60-68HRC;
Density: 7.4 g/cm3;
Micro-Structure: Martensite / Bainite;
Hollow Particles: <5%;
Crack Particle: <5%;
C: 0.8-1.2%;
Cr: No;
Life Time: 3200 Times;
Business Type: Manufacture;
Mn: 0.6-1.2%;
Si: 0.4-1.2%;
S: 0.05;
P: 0.05;
|
Shotblast Type: Shot Blasting;
Shotblast Material: Low Carbon Steel Shot;
Sandblasting Type: Sandblasting Steel;
Shotblast Application: Shipbuilding;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Metallurgy;
Name: Low Carbon Steel Shot;
Life Time: 3200-4000 Times;
Standard: ISO9001/SAE J444;
Sample: Yes,We Can Supply Sample;
Crack Particle: <5%;
C: 0.1-0.3%;
After-Sale Service: Sincere to Solve Customer's Problems;
Micro-Structure: Martensite / Bainite;
Color: Black;
Hollow Particles: <5%;
Business Type: Manufacturer;
Hardness: 40-51HRC;
Shape: Spherical/Round;
Density: 7.4 g/cm3;
Type: Cast Steel;
|
Shotblast Type: Glass Bead Blasting;
Shotblast Material: Glass Beads;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Bridge;
Sandblasting Method: Beads Blasting;
Sandblasting Applications: Glass;
Shape: Round and Smooth;
Wire Diameter: 1.6-1.8mm;
Color: Colorless;
Durability: 3-5 %;
Density: 2.4-2.6g/cm3;
Circularity: Round Rate More Than 95%;
Lead Content: No Lead Content;
Na2o: <14%;
Refractive Index: ND More Than 1.5%;
Flammable Fire Test: Not Easy Combustion;
Microhardness: More Than 650kg/Cm3;
Cao: >8%;
Size Distribution: Oversize Less Than 5% Under Size Less Than 10%;
Appearance: Glass Transparent Without Impurities;
Sio2: >72%;
|
Shotblast Type: Shot Blasting;
Shotblast Material: Steel Grit;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Aircraft Parts;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Metallurgy;
Apprance: Angular;
Cr: 0.26%;
C: 0.8-1.2%;
Diameter: 0.2-2.5mm;
Type: G10-G120;
Fatigue Life: 3000 Times;
Micro-Structure: Martensite;
Business Type: Manufacturer;
Durability: Very Good;
Chemical Composition: C, Si, Mn, S, P, Cr;
Standard: ISO9001,SAE,SGS;
Applications: Casting, Scale Removal of Forging and Heat-Treated;
After-Sale Service: Sincere to Solve Customer's Problems;
Sample: Yes, We Can Provide 500g;
Density: 7.4G/Cm3;
|
Shotblast Type: Shot Blasting;
Shotblast Material: Steel Grit;
Sandblasting Type: Automatic Sandblasting;
Shotblast Application: Aircraft Parts;
Sandblasting Method: Dry Spray;
Sandblasting Applications: Metallurgy;
Apprance: Angular;
Cr: 0.26%;
Micro-Structure: Martensite;
Sample: Yes, We Can Provide 500g;
After-Sale Service: Sincere to Solve Customer's Problems;
Business Type: Manufacturer;
C: 0.8-1.2%;
Diameter: 0.2-2.5mm;
Type: G10-G120;
Standard: ISO9001,SAE,SGS;
Durability: Very Good;
Chemical Composition: C, Si, Mn, S, P, Cr;
Fatigue Life: 3000 Times;
Applications: Casting, Scale Removal of Forging and Heat-Treated;
Density: 7.4G/Cm3;
|