Specification |
Usage: Filling Material, Spinning, Non-Woven Fabric, Uniform Fabric, Paper Industry Material;
Material: Polyamide Fiber (Nylon);
Feature: Anti-Pilling, Abrasion-Resistant, High Hardness;
Fiber Type: Staple;
Pattern: Plain;
Color: White/Black;
Width: 1.5D, 2.5D, 3.5D;
Function: Nylon6 Staple Fibre;
Structure: Round;
Luster: Semi-Dull;
|
Usage: Concrete, Filling Material, Spinning;
Material: Polyvinyl Alcohol;
Feature: Abrasion-Resistant, Anti-Distortion, Heat-Resistant;
Fiber Type: Filament;
Color: Light Yellow;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 15.0 Um;
Breaking Strength: 1600MPa;
Dry Breaking Tenacity(Cn/Dtex)≥: 11;
Hot Water ResistanceºC≥: 104;
E-Modulus (Cn/Dtex)≥: 290;
|
Usage: Concrete, Filling Material, Spinning;
Material: Polyvinyl Alcohol;
Feature: Abrasion-Resistant, Anti-Distortion, Heat-Resistant;
Fiber Type: Filament;
Color: Light Yellow;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 15.0 Um;
Breaking Strength: 1600MPa;
Dry Breaking Tenacity(Cn/Dtex)≥: 11;
Hot Water ResistanceºC≥: 104;
E-Modulus (Cn/Dtex)≥: 290;
|
Usage: Concrete, Filling Material, Spinning;
Material: 100% Polyester;
Feature: Abrasion-Resistant, Anti-Distortion, Anti-Static, Heat-Resistant;
Fiber Type: Filament;
Color: White;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 10~25um;
Modulus of Elasticity: 8000MPa;
Tensile Strength: More Than 900MPa;
Density: 1.36g/cm3;
Material Property: 100%Modified Polyester;
|
Usage: Concrete, Filling Material, Spinning;
Material: 100% Polyester;
Feature: Abrasion-Resistant, Anti-Distortion, Anti-Static, Heat-Resistant;
Fiber Type: Filament;
Color: White;
Width: Provides Custom-Made Service;
Function: High Strength Fiber;
Structure: Miscellaneous Chain Synthetic;
Diameter: 10~25um;
Modulus of Elasticity: 8000MPa;
Tensile Strength: More Than 900MPa;
Density: 1.36g/cm3;
Material Property: 100%Modified Polyester;
|