Specification |
After-sales Service: 7*24 Hours Online Service;
Warranty: 1 Year;
Standard: DIN, CE&ISO&TUV;
Technics: Forging;
Material: a-101,Cr26,Tungsten Carbide;
Application: Co-Rotating Twin Screw Extruder;
Screw Type: Parallel Screw;
Screw Design: Double-Screw;
Wear-Resistance: 2 Times Higher;
|
Standard: DIN, ASTM, GOST, GB, JIS, ANSI, ISO;
Technics: Milling-Drilling-Grinding-Polishing;
Material: Tool Steel, Structural & Engineering Steel etc.;
Base Material: 1.8509, 1.8550, 1.8519, 4140, 5140, 45;
Surface Treatment: Bimetallic, Nitriding, Through-Hardened, Chrome-Pl;
Hardness for Nitriding: >Hv900;
Hardness for Bimetallic: HRC50~70 Depending on Different Alloys;
Thickness of Nitriding Layer: 0.4~0.7mm;
Thickness of Bimetallic: 1.5~3.0mm Depending on Different Alloy Coating;
Application: Extruder;
|
After-sales Service: If Has Quality Defects, a New One Will Be Made.;
Warranty: 180 Days;
Standard: DIN, JIS;
Technics: Cutting, Heat Treatment, Pta Welding, Casting;
Feature: Long Working Life;
Material: Alloy Steel;
|
After-sales Service: If Has Quality Defects, a New One Will Be Made.;
Warranty: 180 Days;
Standard: DIN, JIS;
Technics: Cutting, Heat Treatment, Pta Welding, Casting;
Feature: Long Working Life;
Material: Alloy Steel;
|
Standard: DIN, ASTM, GOST, GB, JIS, ANSI, ISO;
Technics: Milling-Drilling-Grinding-Polishing;
Material: Tool Steel, Structural & Engineering Steel etc.;
Base Material: 1.8509, 1.8550, 1.8519, 4140, 5140, 45;
Surface Treatment: Bimetallic, Nitriding, Through-Hardened, Chrome-Pl;
Hardness for Nitriding: >Hv900;
Hardness for Bimetallic: HRC50~70 Depending on Different Alloys;
Thickness of Nitriding Layer: 0.4~0.7mm;
Thickness of Bimetallic: 1.5~3.0mm Depending on Different Alloy Coating;
|