Specification |
Material: PTFE;
Kind: Color Plastic;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 25-45MPa;
Density: 2.1--2.2 G/M3;
Elongation at Break: 200-350%;
Compression Strength: 24MPa;
Working Temp.: -180~260ºC;
Melting Point: 330ºC;
Produce Max.Temp.: 390ºC;
Fire Resistance: V-0;
Bittle Point Temperature: -268ºC;
Dielectric Strength: >1400kv/mm;
Dielectric Constant: 2.1;
|
Material: Polyurethane;
Kind: Thermosetting Plastic Pipe;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Color: Yellow, Red, Black;
Hardness: 75-95 Shore a;
Elongation: 400%-650%;
Density: 1.12-1.25g/cm3;
ID: 8-12mm;
Od: 10-100mm;
Length: 500mm;
Shape: Round;
|
Material: Polyurethane;
Kind: Thermosetting Plastic Pipe;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Color: Yellow, Red, Black and So on;
Hardness: 75-95 Shore a;
Elongation: 400%-650%;
Density: 1.12-1.25g/cm3;
ID: 8-12mm;
Od: 10-100mm;
Length: 500mm;
Shape: Round;
|
Material: Polyurethane;
Kind: Thermosetting Plastic Pipe;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Color: Yellow, Red, Black;
Hardness: 75-95 Shore a;
Elongation: 400%-650%;
Density: 1.12-1.25g/cm3;
ID: 8-12mm;
Od: 10-100mm;
Length: 500mm;
Shape: Round;
|
Material: Polyurethane;
Kind: Thermosetting Plastic Pipe;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Color: Yellow, Red, Black;
Hardness: 75-95 Shore a;
Elongation: 400%-650%;
Density: 1.12-1.25g/cm3;
ID: 8-12mm;
Od: 10-100mm;
Length: 500mm;
Shape: Round;
|