Specification |
Material: PTFE;
Kind: Color Plastic;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 25-45MPa;
Density: 2.1--2.2 G/M3;
Elongation at Break: 200-350%;
Compression Strength: 24MPa;
Working Temp.: -180~260ºC;
Melting Point: 330ºC;
Produce Max.Temp.: 390ºC;
Fire Resistance: V-0;
Bittle Point Temperature: -268ºC;
Dielectric Strength: >1400kv/mm;
Dielectric Constant: 2.1;
|
Material: POM;
Water Absorption: 0.24%;
Contraction Percentage: <0.4%;
Tensile Strength: 66.6 MPa;
Diameter: 8-350mm;
Color: White, Black, Others;
Density: 1.4G/Cm3;
Market: Euro, Asia, Central and South America;
|
Material: POM;
Water Absorption: 0.24%;
Contraction Percentage: <0.4%;
Tensile Strength: 66.6 MPa;
Diameter: 8-350mm;
Color: White, Black, Others;
Density: 1.4G/Cm3;
Market: Euro, Asia, Central and South America;
|
Material: POM;
Water Absorption: 0.24%;
Contraction Percentage: <0.4%;
Tensile Strength: 66.6 MPa;
Diameter: 8-350mm;
Color: White, Black, Others;
Density: 1.4G/Cm3;
Market: Euro, Asia, Central and South America;
|
Material: PTFE;
Kind: Hard Plastic Rods;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Diameter: 2-350mm;
Color: White, Beige, Black;
Density: 2.1-2.3G/Cm3;
Tensile Strength (Min.): 14MPa;
Crack Elongation (Min.): 140%;
Market: Euro, Asia, Central and South America;
|