Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Instant Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Alumina Block;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block, Alumina;
Usage: Machinery, Chemical, Petroleum, Grind;
Processing Type: Isostatic Pressing Type;
Color: White;
Customized: Customized;
Content: 68/75/92%;
Size: 30mm, 40mm, 50mm, 60mm;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: transitional Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.65~2.7g/cm3;
Apparent Porosity: 20 %;
TSR - in water at 1100ºC: 10-15 Cycle;
Refractoriness Under Load: 1650;
CCS MPa: 80-100;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: transitional Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.65~2.7g/cm3;
Apparent Porosity: 20 %;
TSR - in water at 1100ºC: 10-15 Cycle;
Refractoriness Under Load: 1650;
CCS MPa: 80-100;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Abrasivea, Abrasive Sandblasting, Polishing;
Shape: Sand / Grit / Powder/ Grain / Fineness;
Material: Corundom / Brown Fused Aluminum Oxide;
Grit Available 1: F12, F14, F16, F20, F24, F30, F36, F40, F46, F54;
Grit Available 2: F60, F70, F80, F90, F100, F120, F150, F180, F220;
Chemical Al2O3: Min: 95%, Accept Customized;
Application: Grinding and Fogging Glass, Surface Treatment;
Advantage: Manufacturer, Quality and Price Guaranteed;
Other Name: Brown Fused Alumina, White Fused Aluminum Oxide;
|