Specification |
Structure: Single End;
Pressure: High Pressure Mechanical Seals;
Speed: General Speed Mechanical Seal;
Temperature: Temperature Mechanical Seal;
Performance: High Pressure;
Standard: Standard, Nonstandard;
Type: CS1070t;
Balance: Balanced;
Density: 2.1-2.2g/cm3;
Working Temperature: 200deg;
Compressibility: 8-18%;
Recovery: >40%;
Thickness: 1.0-3.0mm;
|
Structure: Double-End;
Pressure: High Pressure Mechanical Seals;
Speed: High-Speed Mechanical Seal;
Temperature: High Temperature Mechanical Seal;
Performance: High Pressure;
Standard: Nonstandard;
Type: HU7;
Balance: Balanced;
Style: Mechanical Seal;
Material: PU;
Shape (for Gasket): Custom Produce;
Function: Fixed Sealing, Rotary Sealing, Hole Sealing, Du;
Application: Equipment Seal, Pump Seal, Flange Seal, Hydrose;
|
Structure: Double-End;
Pressure: High Pressure Mechanical Seals;
Speed: High-Speed Mechanical Seal;
Temperature: High Temperature Mechanical Seal;
Performance: High Pressure;
Standard: Nonstandard;
Type: HU7;
Balance: Balanced;
Style: Mechanical Seal;
Material: PU;
Shape (for Gasket): Custom Produce;
Function: Fixed Sealing, Rotary Sealing, Hole Sealing, Du;
Application: Equipment Seal, Pump Seal, Flange Seal, Hydrose;
|
Structure: Double-End;
Pressure: Low Mechanical Seal;
Speed: General Speed Mechanical Seal;
Temperature: Low-Temperature Mechanical Seal;
Standard: Standard;
Balance: Balanced;
Thickness: 0.4mm-6mm;
Density: 1.95g/cm3;
Tensile Strenth: >=7.5MPa;
Compressibility: 7-17%;
Recovery: >=35%;
Aging Coefficient: >=0.9;
Creep Relaxation: <=50%;
Ignition Loss: <=30%;
|
Structure: Double-End;
Pressure: Low Mechanical Seal;
Speed: General Speed Mechanical Seal;
Temperature: Low-Temperature Mechanical Seal;
Performance: Temperature;
Standard: Standard;
Balance: Balanced;
Thickness: 0.4mm-6mm;
Color: Red,Black,Gray,Green,Blue,Purple,Yellow,Lightgreen;
Density: 1.95g/cm3;
Work Temperature: 200c;
Tensile Strength: >=5MPa;
Aging Coefficient: >=0.9;
Ignition Loss: <=30;
Compressibility: 7-17%;
Recovery: >=35%;
Creep Relaxation: <=50%;
|