Specification |
Application: Structure Ceramic;
Purity: 99%;
Type: Alumina Piston Pump;
Color: Ivory;
Density: 3.9g/cm3;
Temperature of Application: 1800c;
Advantage: High Temperature Resistance;
Thermal Expansion: 8.5;
Loss Tangent: 2;
Modulus of Elasticity: 350;
Thermal Conductivity: 28;
Abrasion Performance: Excellent;
Key Word: Alumina Ceramic Pump;
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Purity: 99%;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|