Specification |
Content: 75% ~ 80%;
Usage: Construction, Machinery, Grind;
Color: Black;
Customized: Customized;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Grinding Media;
Processing Type: Rolling Type;
Size: Small;
Color: White;
Customized: Non-Customized;
Shape: Round and Cylindrical;
Sample: Availabale;
Place of Origin: Hunan, China;
Feature: High Wear-Resistance and Durable Zirconia Beads;
Name: Zirconia Beads;
Specific Density: 6.02g/cm3;
Moh's Hardness: 9;
Applied Fields: Ink,Coating, Painting,Mineral,Magnetic...;
Weight: 25kg;
Glossiness: 0.2;
Sphericity: 98%;
Composition: 99.9% Zirconia;
Species: Multispecies;
Minimum Order Quantity: 3kg;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Alumina;
Content: >90%;
Usage: Grind;
Processing Type: Rolling Type & Pressing Type;
Size: 30mm,40mm,50mm,60mm;
Color: White;
Equivalent Wear Loss: 0.001%;
Density: 3.65g/cm3;
Hardness: 9 Mohs;
Anti-Compression Strength: 2000MPa;
Al2O3: >=92%;
Fe2o3: <=0.01%;
Water Absorption: 0.01%;
Sio2: 4.51%;
|