Specification |
Standard: Qb;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Rubber, Ceramic, Polyurethane;
Type: Wear Resistant Ceramic;
Feature: Abrasion and Impact Resistance;
Size: Customizable;
Logo: Customizable;
Tear Strength: ≥520kn;
Process: Hot Vulcanizing Process;
Alumina Ceramic Content: 95%;
Name: Wear Resistant Alumina Rubber Ceramic Wear Liners;
Shape: Square, Hexgonal, Cylindrical, Rectangle;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|
Standard: GB;
Application: Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard;
Material: Aluminum;
Type: Wear Resistant Pipe;
Raw Material: 95%Al 2o3;
Ceramic Material: α—al 2o3;
Lining Ceramic Layer Thickness: 4-25mm;
HRC: ≥85;
Refractoriness: 1650ºC;
Maximum Abrasion Impact Strength: 1.6MPa;
Density: 3.62g/cm3;
Thermal Conductivity: 20W/M.K;
|