Specification |
Refractoriness (℃): ≥1810ºC;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Aluminum Chromium Oxide&Spinel;
Features: Anti-Abrasion, Anti-Corrosion, Anti-Oxidation;
Cold Crushing Strength: ≥100MPa;
Density: 3.0~3.2g/cm3;
Apparent Porosity: ≤20%;
Moh's Hardness: 6.7;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Alumina;
Alumina: Sillimatin 60 C 530, Alsint 99.7 C 799;
Size: Od 8-50;
Color: White, Pink Cream;
End: Oec or Beo;
Application: High Temperature Resistant, High Wear Resistance;
Finish: Collar, Slot, Curve;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.1-2.2g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 16cycle;
Rul: 1300;
CCS MPa: 57;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.3-2.35g/cm3;
Apparent Porosity: 15%;
Tsr 950ºC: 15cycle;
Rul: 1500;
CCS MPa: 80;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|