Specification |
Bonding Function: Structural Adhesive;
Morphology: Solvent Free;
Application: Automobile, Construction, Boats, Bus, Truck;
Material: Polyurethane;
Classification: Room Curing;
Characteristic: Electrophoresis up to 230ºC;
Color: Grey;
Curing Mechanism: Poly Reaction;
Color After Mixing: Grey;
Density (Resin): 1.25 G/Cm^3;
Density (Hardener): 1.47 G/Cm^3;
Mix Ratio: 2:1;
Application Time After Mixing: 10-15 Min;
Curing Condition (23ºC): 168 H;
Electrophoresis: up to 230ºC;
Tensile Strength: 3.5 MPa;
Shear Strength: 2.5 MPa;
Elongation at Break: 450%;
|
CAS No.: 7085-85-0;
Formula: C3h8n2o;
EINECS: 231-545-4;
Bonding Function: High Temperature Resistant Adhesive;
Morphology: Solid-State;
Application: Woodworking, Footwear & Leather, Fiber & Garment, Sofa, Mattress, Fabric etc.;
Material: Apao;
Classification: Hot Melt;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: White;
Appearance: Milky White Solid;
Smell: Good Smell;
Softening Point: 120-140 Centigrade;
Melt Viscosity: 1600-3000PA.S at 70 Centigrade;
Flash Point: >392 Degrees F , 200 Centigrade;
Recommended Temperature: 165-180 Centigrade;
Shelf Life: 2 Years;
Relative Density: 0.88-0.96;
|
Bonding Function: Pressure sensitive Adhesive;
Morphology: Water Emulsion;
Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, BOPP Tape;
Material: Acrylic;
Classification: Pressure-Sensitive;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: White;
Polymer Type: Acrylic Copolymer;
Appearance: Pure White;
Holding Force: >=24 Hours;
Total Solid Content by Wt: 54.0%-56.0%;
pH Value at 25 Degrees Celsius: 6.1-9.0;
Viscosity(Mps/S): <=80;
Initial Adhesivion Force(GB): >=23#;
Coating Backer: BOPP, PVC, Pet Film, Paper, Masking Tape etc;
|
CAS No.: 63148-60-7;
EINECS: 230-391-5;
Bonding Function: Structural Adhesive;
Morphology: Solid-State;
Application: Automobile, Construction, Woodworking, Packing, Wood Assembly, Ceramic Tile, Drywall, Plywood etc.;
Material: Chloroprene;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Transparent;
Viscosity: >100, 000 Cps;
Solid Content: 75%-85%;
Completely Solidfication Time: 12-48 Hours;
Final Adhesion: >3 MPa;
Adaptive Temperature: -30-80 Degrees Celsius;
Construction Temperature: -20-35 Degrees Celsius;
Adhibition: Prefinished Panels, Bathroom Fixtures etc;
|
Bonding Function: Shoes Making Glue;
Morphology: Solvent;
Application: Automobile, Construction, Footwear & Leather, Fiber & Garment, Packing, Shoes Repairing;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Clear;
Appearance: Colorless Transparent Liquid;
Solid Content: 13% - 15%.;
Viscosity: 1000 - 2000cps.;
Density: 0.83-0.92kg/L.;
Tack Time: Short;
|