Specification |
Bonding Function: Structural Adhesive;
Morphology: Solvent Free;
Application: Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Elastomer;
Characteristic: Waterproof;
Color: Parquet Brown;
Chemical Base: Polyurethane;
Density: ~1.4 Kg/L;
Skinning Time: ~50 Minutes;
Curing Rate: ~2.5 mm/24h;
Service Temperature: -40°c to+80°c;
Shear Strength: ~0.8 N/mm^2;
Tensile Strength: ~1.6 N/mm^2;
Shore a Hardness: ~42;
Elongation at Break: ~550%;
Advantage: Solvent Free;
Advantage-1: Fast Curing;
Advantage-2: Easy to Scrape;
Advantage-3: Environmental Friendly;
Colour: Ochre;
Bonding: Fullsurface;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|