Specification |
Material: Edpm;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Model No.: EVA Foam.PE Foam;
Hardness Shore C: 15-35;
Tensile: >3 MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Burning Speed: 50 mm/Min;
|
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: ≤1.5;
Tensile Strength: 12-20MPa;
Thickness (Mm): 1-30mm;
Width (Mm): 1220, 1560, 2050;
Length (Mm): 2440, 3050;
Color: White, Black, Red, Blue, Yellow, Green, Gray;
Style: PVC Freee Foam Board, PVC Celuka Foam Board,;
Packaging Detail: : PE Film Package for Several Sheets;
Delivery Detail: 5 - 10 Days;
|
Material: PVC;
Kind: White Plastic Sheet;
Water Absorption: <1.5%;
Contraction Percentage: <0.4%;
Tensile Strength: 12-18 MPa;
Width: 1.22m 0.915m 1.56m 2.05m;
Product: PVC Foam Board;
Thickness: 1-40mm;
Lengrh: as Customized;
Color: White;
Apparent Density: 0.45-1 G/M3;
Shao Scale: 50-80 D Type;
Flexural Strength: 12-18 MPa;
Impact Strength: 8-15kj/M2;
Water Absorbing Rate: <1.2%;
|
After-sales Service: If Any Problem, Please Kindly Let Us Know Within 6;
Warranty: If Any Problem, Please Kindly Let Us Know Within 6;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: 0.19%;
Contraction Percentage: 0.4%~1.4%;
Tensile Strength: 12MPa;
Size: 1220*2440mm, 1560*3050mm, 2050*3050mm;
Thickness: 1mm-5mm;
Density: 0.45-0.9g/cm3;
Color: White or Color;
Bending Strength: 20MPa;
Compressive Strength: 4MPa;
Elogation at Break: >15%;
Flexual Modulus: >800 MPa;
|
After-sales Service: If Any Problem, Please Kindly Let Us Know Within 6;
Warranty: If Any Problem, Please Kindly Let Us Know Within 6;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: 0.19%;
Contraction Percentage: <0.4%;
Tensile Strength: 12MPa;
Size: 1220X2440mm/2050*3050mm;
Thickness: 1mm-50mm;
Density: 0.38-1.1g/cm3;
Color: White or Color;
Bending Strength: 20MPa;
Compressive Strength: 4MPa;
|