Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 72%;
Alloy: Alloy;
Type: Inconel Bar;
Powder: Not Powder;
Resistance: 1.5;
Ultimate Strength: 760MPa;
Elongation: 30%;
Melting Point: 1393-1427;
Shape: Wrie, Sheet, Pipe, Bar;
Material: Ni, Cr, Fe;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, DIN, ASTM;
Purity: 80%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Resisivity: 0.55;
Density: 8.6cm3;
Curie Point: 450 C;
Saturation Magnetostriction Coefficient: 2;
Hardness: 120~210 Hv;
Tensile Strength: 560~1030 MPa;
Yield Strength: 150~980 MPa;
Elongation: 3~50 %;
Use: High Frequency Inductive Components;
|