Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 58%;
Alloy: Alloy;
Type: Inconel Tube;
Powder: Not Powder;
Resistance: 1.11;
Ultimate Strength: 830MPa;
Elongation: 30%;
Melting Point: 1390-1420;
Shape: Wrie, Sheet, Pipe, Bar;
Material: Ni, Cr, Fe;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Density: 8.47;
Elongation: 2~5;
Sample: Free;
Technology: Cold Drawing;
Melting Range: 1354-1413c;
Tensile Strength: 1170-1520MPa;
Yield Strength: 1035-1450MPa;
Surface: Bright/Acid White/Oxidation;
Condition: Soft Annealed/Hard;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: ASTM;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Foam;
Powder: Not Powder;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Density: 8.19 G/M³;
Elongation: 2~5;
Sample: Free;
Technology: Cold Drawing;
Melting Range: 1354-1413c;
Tensile Strength: 1170-1520MPa;
Yield Strength: 1035-1450MPa;
Surface: Bright/Acid White/Oxidation;
Condition: Soft Annealed/Hard;
Max Temp: 1300 F (704 C);
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 63%;
Alloy: Non-alloy;
Type: Nickel Bar;
Powder: Not Powder;
Melting Point: 1300~1390;
Surface: Bright/Oxidation;
Elongation (A5%): 35;
Tensile Strength: 480MPa;
Yield Strength: 170MPa;
Hb: Min 331;
Density: 8.9g/cm3;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Size: 10~200mm;
|