| Specification |
Material: Round Steel;
Content: >90%;
Usage: Mill, Grinding;
Processing Type: Forged, Rolling Type;
Size: Dia.1"-5";
Color: Metallic Color;
Customized: Customized, Non-Customized;
Hardness: HRC 60-65;
Breakage Rate: 1% Max;
Heat Treatment: Quenching/Tempering;
Impact Toughness: ≥12ak.J/Cm2;
Microstructure: M+B+C;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|