Specification |
Material: Steel Scrap, Ferrochrome;
Content: >90%;
Usage: Mill, Grinding;
Processing Type: Casting Type;
Size: Dia. 17mm-130mm;
Color: Black;
Customized: Customized, Non-Customized;
Hardness: HRC 58-63;
Breakage Rate: 1% Max;
Heat Treatment: Oil Quenching;
Impact Toughness: ≥5ak.J/Cm2;
Microstructure: M+C;
|
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type;
Size: Middle;
Color: White;
Customized: Customized;
MOQ: 10;
Ceramic Mohs Hard: 9;
Ceramic Corrosion: Resistance: Wonderful;
Use for: Lining of Equipment and Pipe;
|
Material: Alumina;
Content: 75% ~ 80%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >75;
Fe2o3(%): <0.4;
Sio2(%): <20;
Mohs Hardness: 8;
Water Absorption: <0.01;
Bulk Density(g/cm3): >3.15;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >800n;
Diameter: 0.5-13mm;
Sphericity: >95%;
|
Material: Alumina;
Content: 75% ~ 80%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >75;
Fe2o3(%): <0.4;
Sio2(%): <20;
Mohs Hardness: 8;
Water Absorption: <0.01;
Bulk Density(g/cm3): >3.15;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >800n;
Diameter: 0.5-13mm;
Sphericity: >95%;
|
Material: Alumina;
Content: 75% ~ 80%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >75;
Fe2o3(%): <0.4;
Sio2(%): <20;
Mohs Hardness: 8;
Water Absorption: <0.01;
Bulk Density(g/cm3): >3.15;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >800n;
Diameter: 0.5-13mm;
Sphericity: >95%;
|