Specification |
Material: Steel Scrap, Ferrochrome;
Content: >90%;
Usage: Mill, Grinding;
Processing Type: Casting Type;
Size: Dia.1"-5";
Color: Black;
Customized: Customized, Non-Customized;
Hardness: HRC 58-63;
Breakage Rate: 1% Max;
Heat Treatment: Oil Quenching;
Impact Toughness: ≥5ak.J/Cm2;
Microstructure: M+C;
|
Material: Zro2, Sio2;
Usage: Construction, Machinery, Grind;
Processing Type: Rolling or Isostatic Pressing;
Size: 0.4~5mm;
Color: Cream;
Customized: Customized;
Featrue: High Hardness, High Density and Anticorrosion;
Application: Mining Machine;
Grinding Situation: Dry Grinding, Wet Griding;
Field: Cement, Chemical, Paints, Inks, Dyes;
OEM: Accept;
Specific Gravity: 4.0~4.2g/cm3;
Vickers Hardness: 1000~1050;
Water Absorption: 0%;
Application Industry: Ceramics, Minerals, Ores;
|
Material: Ceramics;
Content: Zirconium Silicate;
Usage: Grind;
Processing Type: Rolling Type;
Size: Small;
Color: White;
Customized: Customized;
Item: Ceramic Beads as Grinding Media;
Materials: Zirconium Silicate;
Feature: Excellent Grinding Efficiency;
Application: Ball Mill, Pot Mill, Librating Mill, Pebble Mill;
Field: Mineral, Metallurgy, Porcelain, Enamel;
OEM: Accept;
Producing Way: by Roll;
Chemical Composition: Al2O3 + Zro2+ Sio2;
Density: 4.0g/Cn3;
Moh's Hardness: 8;
Vickers Hardness Hv5: 1000~1050;
Diameter Range: 0.5~20mm;
Roundness(Xmin/Xmax): 93%;
Water Absorption: 0;
Package: Bags+ Plywood Case;
|
Material: Ceramics;
Content: 95% 90% 92% 68%;
Usage: Grind;
Processing Type: Isostatic Pressing Type;
Size: 2mm ~70mm for Ball , 21mm 31mm for Cylinder;
Color: White;
Customized: Customized;
Item: Alumina Grinding Balls;
Materials: Alumina;
Alumina Content: 92% 95% 68% 55%;
Type: High-Alumina;
Diameter: 1mm-70mm;
Grinding Situation: Dry Grinding, Wet Griding;
Feature: High Hardness, High Density and Anticorrosion;
Application: Ball Mill, Pebble Mill, Mining Grinding;
Field: Ceramic, Metallurgy, Glass, Porcelain, Enamel;
OEM: Accept;
|
Material: Zro2 Sio2;
Content: Zro2:55~65% Sio2:30~35%;
Usage: Construction, Machinery, Grind;
Processing Type: Rolling or Isostatic Pressing;
Size: 2~20 mm;
Color: White;
Customized: Customized;
Application: Grinding Mineral Materials;
Delivery Time: 20days;
Water Absorption: 0;
Self Abrasion: <0.01~0.02;
|