| Specification |
CAS No.: 7085-85-0;
Application: Construction, Woodworking;
Material: 100% Silicone;
Classification: Other Adhesives;
Other Names: Silicone Sealant;
Keywords: Cheap Silicone Sealant Adhesive;
Advantages: Excellent Anti-Age, Good Adhesion;
Full Cure Time: 24~48h;
Shelf Life: 9~12 Months at 25degrees Centigrade;
Tack Free Time: 30~40mins;
Main Raw Material: Silicone;
Type: Acetic;
Colors: Clear,White, Black;
Packing: 310ml/Cartridge,600ml/Sausage;
Product Name: Gp Silicone Sealant;
Einecs No.: 210-898-8;
Mf: Mixture;
Package: Sausage or Cartridge;
|
CAS No.: 7085-85-0;
Formula: Mixture;
EINECS: 230-391-5;
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: White;
Sample: Free Sample;
OEM: Yes;
Shelf Life: 12 Month;
|
CAS No.: 7085-85-0;
Formula: Mixture;
EINECS: 230-391-5;
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: White;
Sample: Free Sample;
OEM: Yes;
Shelf Life: 12 Month;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|
Bonding Function: Urethane Sports-Turf Adhesive;
Morphology: Solvent Free;
Application: Construction, Synthetic Turf;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Green;
Uses: Artificial Turf Installation Adhesive;
Curing Mechanism: Moisture-Curing;
Viscosity: 50000±5000;
Density: 1.35±0.1 Kg/L;
Tack-Free Time: 60 - 100 Min;
Solid Content: 100%;
Shore a Hardness: 50 - 60;
Tensile Strength: 1.5 - 2.0 MPa;
Elongation at Break: 200 % - 300 %;
Set to Light Foot Traffic: ~ 12 Hours;
|