Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Packing Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃, 1360c;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Name: 1260c Ceramic Fiber Blanket;
Density: 96kg/M3 or 128kg/M3 or 160kg/M3;
Working Temperature: 1100-1430;
Length: 3600mm, 7200mm, or Other Customer's Request;
Width: 600mm, 610mm;
Thickness: 10mm~50mm;
Chemical Composition: Al2O3, Sio2;
Maximum Working Temperature: 1260c;
Color: White;
Fiber Diameter: 3-5um;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Inorganic Hardened Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: 1260 Ceramic Fiber;
Color: White;
Rupture Strength(MPa): 0.6;
Ignition Lost (at 1000ºCx5hr) Lol%: 8;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
|