Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Packing Material, High Temperature Insulating Material;
Temprature Classification: 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Bulk;
Manufacturing Technique: Swinging and Blowing Technology;
Kind: Ordinary Ceramic Fiber;
Ultimate Strength (≥ MPa): 0.08-0.12;
Thermal Conductivity: 0.16--0.20 W/(M.K);
Al2O3: 43-52%;
Sio2: 46-57%;
Color: White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Insulation Board;
Application: Refractory;
Thickness: 10-50mm;
Width: 1000/600/300mm;
Length: 1200/1000/900/600mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1100c/1260c/1360c/1430c;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
Keyword: Refractory Ceramic Fiber Board Heat Insu;
Type: Containing Zirconium Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Polycrystalline Mullite Boards;
Application: Refractory;
Thickness: 10-50mm;
Width: 1000/600/300mm;
Length: 1200/1000/900/600mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1100c/1260c/1360c/1430c;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Keyword: Refractory Ceramic Fiber Board Heat Insu;
Density (Kg/M³ ): 160;
Color: Pure White;
Type: Polycrystalline Mullite Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Insulation Board;
Application: Refractory;
Thickness: 10-50mm;
Width: 1000/600/300mm;
Length: 1200/1000/900/600mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1100c/1260c/1360c/1430c;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
Keyword: Refractory Ceramic Fiber Board Heat Insu;
Type: Containing Zirconium Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2, Zro2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Bio Soluble Fiber Blanket;
Application: Industrial Furnace;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600-14640mm;
Chemical Composition: Al2O3+Sio2+Zro2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 64/80/96/128/160kg/M3;
Color: Pure White;
|