Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 90%;
Alloy: Alloy;
Type: Copper Nickel;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Extensibility: Min15;
Temperature Range: 10~80c;
Resistivity: 0.35+/-0.05ohm/M;
Density: 8.7g/Cm;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 35%-38%;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Surface: Bright;
Chemical Composition: Ni, Fe, Co;
Density: 8.1 g/cm3;
Treatment: Hydrogen Annealing;
Size: Customized;
Grade: Nickel Base Alloy;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: ASTM;
Purity: 58%;
Alloy: Alloy;
Type: Hastelloy Wire;
Powder: Not Powder;
Chemical Composition: Ni Cr Mo Fe W Co;
Resistance: 1.5;
Ultimate Strength: 690MPa;
Elongation: 40%;
Melting Point: 1325-1370;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: ASTM;
Purity: 58%;
Alloy: Alloy;
Type: Hastelloy Wire;
Powder: Not Powder;
Chemical Composition: Ni Cr Mo Fe W Co;
Resistance: 1.5;
Ultimate Strength: 690MPa;
Elongation: 40%;
Melting Point: 1325-1370;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: ASTM;
Purity: 58%;
Alloy: Alloy;
Type: Hastelloy Wire;
Powder: Not Powder;
Chemical Composition: Ni Cr Mo Fe W Co;
Resistance: 1.5;
Ultimate Strength: 690MPa;
Elongation: 40%;
Melting Point: 1325-1370;
|