Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Density: 8.47;
Elongation: 2~5;
Sample: Free;
Technology: Cold Drawing;
Melting Range: 1354-1413c;
Tensile Strength: 1170-1520MPa;
Yield Strength: 1035-1450MPa;
Surface: Bright/Acid White/Oxidation;
Condition: Soft Annealed/Hard;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|