Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 78%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Density: 8.4 g/cm3;
Elongation: 20;
Delivery Time: 7 Working Days;
Max Continuous: 1200;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright, Acid White, Oxidation;
Condition: Soft Annealed;
MOQ: 3kg;
|
Application: Industrial;
Standard: GB;
Purity: Ni 95%, Al 5%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Size: 1.6mm;
Spool: D 300;
Wire Weight: 15kg Each Spool;
Equal to: Tafa 75b;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|
Application: Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Surface: Bright;
Condition: Hard (Y)/ Soft (M)/Half Hard;
Equal to: Hyra 80;
Resistivity: 0.55;
Density(g/cm3): 8.6g/cm3;
Elongation (≥ %): 15-25;
Grade: 1j79;
Feature: High Initial Permeability;
Ni (Min): 80;
|
Application: Industrial;
Standard: JIS, GB, ASTM;
Purity: >99.5%;
Alloy: Non-alloy;
Type: Nickel Strip;
Powder: Not Powder;
Density: 8.9(g/cm3);
Surface: Bright;
Size: 0.01-3mm*0.5-300mm;
Status: Soft, Hard, Half Hard;
Specific Heat: 0.109(456 J/Kg.ºC);
Electrical Resistivity: 0.096×10-6ohm.M;
Melting Point: 1435-1446ºC;
Thermal Conductivity: 70.2 W/M-K;
Mean Coeff Thermal Expansion: 13.3×10-6m/M.ºC;
|