| Specification |
Material: Natural Rubber;
Feature: Wear-resistant, Heat-resistant;
Color: Black Rubber Sheet;
Inter Diameter: 100~1300mm;
Length: 1m~12m;
Capacity: Rubber Hose for Sand and Grit Blasting;
|
Material: UHMWPE Top Cover,Rubber Cushion,Alumina T Slot;
Usage: Used at Conveyor Feed Point;
Feature: Wear-resistant, Impact-resistant, Tear Resistant;
Raw Materials: UHMWPE,Rubber,Alumina T Slot;
Medium: None;
Performance: Impact Absorbing, Slick UHMWPE Surface;
Color: Red,Black, etc.;
Product Material: UHMWPE Cap,Cushion Rubber,Alloy Framework,T-Slot;
Process: Hot Vulcanization Process;
Installation Assemble Parts: T-Slot,Nut and Washer;
Product Usage: to Reduce Shock and Damage to Conveyor Belt;
|
Material: Natural Rubber;
Usage: Pulley Lagging Rubber Sheet;
Raw Materials: Natural Rubber, Pad;
Type: Pulley Lagging;
Product Usage: Reduce Slippage & Extend Service Life of Conveyor;
Product Material: Nr, Br & Fras Approved Rubber;
Cn Bonding Layer: with Cn Bonding Layer;
Hardness: 70±5 Shore a;
Abrasion Loss: <160mm3;
Thickness: 8, 10, 2, 15, 20mm, etc;
Length: 10 Meters Packed in Roll or as Per Customers' Requ;
|
Material: Natural Rubber;
Usage: Eliminate Belt Slippage, Increase Pulley Life;
Feature: Wear-resistant, Impact-resistant, Tear Resistant;
Raw Materials: Natural Rubber, Pad;
Medium: None;
Performance: None;
Color: Black Rubber Surface, Green Cn Layer;
Rubber Pulley Lagging Cn Layer: New Type Cn Layer, No Need to Roughen;
Lagging Cn Layer Peeling Strength: >12 Kn/M;
Rubber Pulley Lagging Abrasion Loss: <80mm3;
Rubber Pulley Lagging Size: 10m*2m Without Any Splice, Custom Thickness;
Rubber Lagging Mold: 10m*2m;
Rubber Lagging Installation: Easily, No Need Removing Pulleys From Conveyor;
Elongation at Break: >880%;
|
Material: Natural Rubber;
Usage: Industrial, Eliminate Belt Slippage, Increase Pulley Life;
Feature: Wear-resistant, Impact-resistant, Heat-resistant, Corrosion-resistant, Insulating, Cold-resistant, Tear Resistant;
Raw Materials: Natural Rubber, Pad;
Medium: None;
Performance: None;
Color: Black;
Alumina Oxide: >92%;
Ceramic Hardness(Mohs): >9t;
Working Temperature: <85 Degree;
Rubber Hardness: 65+/-5 Shore a;
Tensile Strength: 24 MPa;
Cn Bonding Layer Peel Strength: >12kn/M;
|