Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: 28%~40%;
Cold Crushing Strength: ≥50MPa;
Apparent Porosity: ≤23%;
Cao: ≤2.0%;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block, Square, Hexagon, Circular, Triangle, etc.;
Usage: Filter Material, High Temperature Insulating Material, Industrial Ceramic;
Chemical Composition: Al2O3.Sio2;
Temprature Classification: 1350ºC;
Kind: Industry Ceramic;
Bulk Density(Kg/M3): 500-680;
Middle Wall Thickness(mm): 0.3;
Thermal Expansion Coefficient(in/Ink): 1.5- 1.8;
Thermal Shock Resistance (K): Max 500;
Height(mm): 50;
Average Weight Per Piece(Kg): 0.3;
Specific Heat Capacity(J/Kgk): 850- 1000;
Water Absorption %: 20-25;
|
Shape: Cuboid, Square, Roundness;
Place of Origin: Jiangxi, China;
Model Number: BS-Ihcp;
Packaging Details: Plastic Woven Bag, Carton Box, Wooden Box, etc;
Usage: Automobile Exhaust System;
Water Absorption: 50.4%;
Open Porosity: 61%;
Specific Gravity: 0.6-0.9g/cm3;
Thermal Expansion Coefficient: 1.5-3(X10-6K-1);
Temperature Softening: >1280ºC;
Cooking Surface Temperature: 1000-1200ºC;
Co Release: <=0.006%;
Nox Release: <=5ppm;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition: Al2O3.Sio2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c, 1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|